Unbelievable Bending Super-thick Steel Plate Process – 160 mm Steel Sheet

Bending is a manufacturing process that produces a V-shape, U-shape, or channel shape along a straight axis in ductile materials, most commonly sheet metal. Commonly used equipment include box and pan brakes, brake presses, and other specialized machine presses. Typical products that are made like this are boxes such as electrical enclosures and rectangular ductwork.

Bending Thick Steel Plate

Bending thick steel plates to a tight radius is not an easy task.  There are many variables to consider such as thickness, surface and edge condition, as well as the material’s chemical composition. Plate bending, also referred to as plate rolling, is a process whereby a force is applied to a plate causing deformation along the bending axis forcing the plate to bend at a desired angle.  At that moment of bend, the material is experiencing tension, wherein it expands on the outside surface of the bend, and compresses, or shrinks, on the inside.

Upon the release from the bending force, the residual stress in the material will cause the plate to spring-back. To compensate for the spring-back, plate needs to be bent to a greater angle than the angle required.  An experienced operator can calculate the amount of spring-back to be expected based on several factors, helping to speed material construction with fewer attempts.

Typically, plate bending is performed on a press-brake. A press brake contains two tools: the upper tool – known as “the punch” and the lower tool – known as “the die”.  The plate to be bent has to be positioned over the die and held in place while the punch is lowered onto the plate and the applied force causes it to bend. The bend angle is controlled by the depth to which the punch forces the plate into to the die. Most common plate bending is called V-bending where the used punch and die tools are V-shaped.

When the punch does not push the material all the way to the bottom of that die cavity, leaving a space underneath, then we have “air bending”, and when the punch pushes the material all the way to the bottom of the die cavity then we have “bottoming”.  The bottoming process allows more control over the bent angle do to the lower occurrence of springback. What also needs to be remembered while bending on the press brake, is that the thicker and harder the plate is, it will require a larger minimum bend radius.

In the video below, we can see Bending Super-thick Steel Plate Process – 160 mm Steel Sheet
Thank you for visiting our website! We hope you found something that sparked interest on our website